YIG (Y3Fe5O12) Sputtering Target
Release Date[2013-6-5 15:56:26]    Total access[803]Times
 

Yttrium Iron Garnet (YIG) Sputtering Target

Magnetic properties of YIG (Y3Fe5O12) thin films prepared by the post annealing of amorphous films deposited by rf-magnetron sputtering

We report magnetic properties of Y3Fe5O12 (YIG) films on thermally oxidized Si (100) and (Gd3Ga5O12) GGG (111) substrates. Amorphous YIG films with the cation ratio Y:Fe=3.04:4.96, deposited by rf-magnetron sputtering at room temperature in pure argon atmosphere, were crystallized by postannealing (600�900 �C) of amorphous films in air and in 500 ppm oxygen. While postannealed YIG films on GGG substrates were well textured, those on Si (100) were randomly oriented. High-quality YIG films could be better obtained in the reduced (500 ppm O2) oxygen atmosphere than air since more effective YIG growth during annealing process and lower FMR linewidth (?H) of films could be achieved.

Yttrium Iron Garnet YIG is generally immediately available in most volumes. High purity, submicron and nanopowde forms may be considered. American Elements produces to many standard grades when applicable, including Mil Spec (military grade); ACS, Reagent and Technical Grade; Food, Agricultural and Pharmaceutical Grade; Optical Grade, USP and EP/BP (European Pharmacopoeia/British Pharmacopoeia) and follows applicable ASTM testing standards. Typical and custom packaging is available. Additional technical, research and safety (MSDS) information is available as is a Reference Calculaton for converting relevant units of measurement.

Thin films of Yttrium Iron Garnet (YIG) are grown by radio frequency magnetron non reactive sputtering system. Thin films are crystallised by heat-treatment to obtain magneto-optical properties. On quartz substrate, the network of cracks observed on the annealed samples can be explained by the difference between the thermal expansion coefficient of substrate and YIG. The Faraday rotation of thin films is measured with a classical ellipsometric system based in transmission which allows us to obtained an accuracy of 0.01属. We studied the variation of Faraday rotation versus the applied magnetic field. The variation of the Faraday rotation is the same that this obtained by VSM (vibrating sample magnetometer) analysis. With a quartz substrate, maximum Faraday rotation is observed to be 1900属/cm at the wavelength of 594 nm for an annealing of 740属C. The variation of the Faraday rotation versus the wavelength is studied. The obtained values are comparable to those of the literature for the bulk material. In order to eliminate the stress due to the heat-treatment, we made some films on Gadolinium Gallium Garnet (GGG) which thermal expansion coefficient is near than the YIG one. The material crystallises with no cracks and the Faraday effect is equivalent.

 

 